Pandan deformation frèt, plastisit la se mwayen, machinabilite a ak soudabilite yo akseptab, men pati yo bezwen prechofe a plis pase 200 degre anvan soude. Fil fè desen ak frèt tit ak pwosesis tretman chalè pèfòmans se yon bon bagay, pi wo hardenability, nan lwil oliv kritik trempe dyamèt la nan 6.5 ~ 18mm, trempe deformation se ti, men gen surchof, sansiblite dekarbonizasyon ak tanperaman frajil. Asye a apeze gen gwo fòs, severite ak rezistans mete, ak bon fòs estatik ak fòs fatig.

Konpozisyon chimik pousan nan analiz louch klas 30Mn2.

C(％)	Si(％)	Mn(％)
0.27-0.34	0.17-0.37	1.40-1.80

30Mn2

Pwopriyete mekanik nan klas 30Mn2
Prèv fòs Rp0.2 (MPa)	Fòs rupture Rm (MPa)	Enèji enpak KV (J)	Elongasyon nan ka zo kase A(pousan)	Rediksyon nan koup transvèsal sou ka zo kase Z(pousan)	Kòm-Chalè-trete Kondisyon	Brinell dite (HBW)
578 (Pi gran pase oswa egal a)	359 (Pi gran pase oswa egal a)	43	12	14	Solisyon ak Aje, Recuit, Ausaging, Q plis T, elatriye	212

Pwopriyete fizik klas 30Mn2
Pwopriyete	Dansite kg/dm3	Tanperati T degre /F	Chalè espesifik J / kgK	Konduktivite tèmik W/mK	Rezistans elektrik µΩ·cm	Modil elastisite kN/mm2
258 (Pi gran pase oswa egal a)	283 (Pi gran pase oswa egal a)	23	42	14	Solisyon ak Aje, Recuit, Ausaging, Q plis T, elatriye	143
Tanp. degre / degre F	Limit souch ranpe (10000h) (Rp1,0) N/mm2	Fòs rupture ranpe (10000h) (Rp1,0) N/mm2
855	436	912

30Mn2 Gamme de pwodwi yo
Kalite pwodwi	Pwodwi yo	Dimansyon	Pwosesis yo	Delivre estati
Plak / Fèy	Plak / Fèy	0.08-200mm(T)WL	Forge, woule cho ak woule frèt	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED, piki eksplozif
Steel Bar	Bar wonn, Bar plat, Bar kare	Φ8-1200mm*L	Forge, woule cho ak woule frèt, jete	Nwa, vire graj, eksplozif piki,
Bobin / retire rad sou ou	Steel bobin / Steel Strip	{{0}}.03-16.0x1200mm	Fwad-woule ak cho-woule	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED, piki eksplozif
Tiyo / Tib	Tiyo san pwoblèm / Tib, Tiyo soude / Tib	OD:{{0}}mm x WT:0.5-20.0mm	Ekstrisyon cho, frèt trase, soude	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED