20CrNiMoH estriktirèl Steel

konpozisyon hemical pousan nan analiz louch klas 20CrNiMoH

C(％)	Si(％)	Mn(％)	P(％)	S(％)	Cr(％)	Ni(％)	Mo(％)	B (pousan)	Ti(pousan)
0.17-0.23	0.17-0.37	0.60-0.95	0.035	0.035	0.35-0.65	0.35-0.75	0.15-0.25	—	—

20CrNiMoH

Pwopriyete mekanik nan klas 20CrNiMoH

Prèv fòs Rp0.2 (MPa)	Fòs rupture Rm (MPa)	Enèji enpak KV (J)	Elongasyon nan ka zo kase A(pousan)	Rediksyon nan koup transvèsal sou ka zo kase Z(pousan)	Kòm-Chalè-trete Kondisyon	Brinell dite (HBW)
173 (Pi gran pase oswa egal a)	651 (Pi gran pase oswa egal a)	14	22	41	Solisyon ak Aje, Recuit, Ausaging, Q plis T, elatriye	133

Pwopriyete fizik klas 20CrNiMoH

Pwopriyete	Dansite kg/dm3	Tanperati T degre /F	Chalè espesifik J / kgK	Konduktivite tèmik W/mK	Rezistans elektrik µΩ·cm	Modil elastisite kN/mm2	To ekspansyon
393 (Pi gran pase oswa egal a)	822 (Pi gran pase oswa egal a)	13	42	32	Solisyon ak Aje, Recuit, Ausaging, Q plis T, elatriye	311
Tanp. degre / degre F	Limit souch ranpe (10000h) (Rp1,0) N/mm2	Fòs rupture ranpe (10000h) (Rp1,0) N/mm2
282	394	521

20CrNiMoH Gamme de pwodwi yo

Kalite pwodwi	Pwodwi yo	Dimansyon	Pwosesis yo	Delivre estati
Plak / Fèy	Plak / Fèy	0.08-200mm(T)*W*L	Forge, woule cho ak woule frèt	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED, piki eksplozif
Steel Bar	Bar wonn, Bar plat, Bar kare	Φ8-1200mm*L	Forge, woule cho ak woule frèt, jete	Nwa, vire graj, eksplozif piki,
Bobin / retire rad sou ou	Steel bobin / Steel Strip	{{0}}.03-16.0x1200mm	Fwad-woule ak cho-woule	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED, piki eksplozif
Tiyo / Tib	Tiyo san pwoblèm / Tib, Tiyo soude / Tib	OD:{{0}}mm x WT:0.5-20.0mm	Ekstrisyon cho, frèt trase, soude	Rekwit, solisyon ak aje, Q plis T, ACID-WASHED