GB 60SI2MN Steel se yon kalite siperyè Alloy Spring Steel, Li fè pati segondè bon jan kalite segondè kabòn alyaj Spring Steel. Trempe & Trempe Dite se 28-34 HRc. 60SI2MN asye Recuit livrezon hardenss mwens pase 250HB.
Konpozisyon chimik
| C(％) | 0.56-0.64 | Si(％) | 1.50-2.00 | Mn(％) | 0.60-0.90 | P(％) | Mwens pase oswa egal a 0.035 |
| S(％) | Mwens pase oswa egal a 0.035 | Cr(pousan) | 0.35max | Ni(pousan) | 0.35max |
Ekivalan a 60SI2MN alyaj Spring Steel
| USA | Almay | Lachin | Japon | Lafrans | Angletè | Itali | Polòy | ISO | Otrich | Syèd | Espay |
| AISI/SAE/ASTM/UNS | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | ISO | ONORM | SS | UNE |
| 60Si7 / 1.0909 | 60Si2Mn | 60SI2MN | 60S7 | 61SiCr7 | |||||||
Tretman chalè ki gen rapò
- Recuitnan 60SI2MN Spring Steel
Dousman chofe a 740-770 degre epi pèmèt ase fwa, kite asye a byen chofe, Lè sa a, fre dousman nan gwo fou a. Asye zouti 60SI2MN a pral jwenn MAX 250 HB (dite Brinell).
- Redi nan 60SI2MN Spring Steel
60SI2MN asye yo ta dwe chofe inifòm nan 830-860 degre (1526-1580 degre F) jiskaske yo konplètman chofe. Apeprè 30 min pou chak 25 mm nan seksyon desizyon yo dwe bay ak Lè sa a, asye yo ta dwe imedyatman etenn nan lwil oliv. Jwenn dite 61 Min.
- Tanperaman nan 60SI2MN Spring Steel
Tanperaman nan asye 60SI2MN fèt nan 480-530 degre, tranpe byen nan tanperati a chwazi ak tranpe pou omwen yon èdtan pou chak 25mm nan epesè total. Valè dite nan diferan tanperati apre tanperaman HRC: 150 degre -61HRc, 200 degre -60HRC, 300 degre -56HRC, 400 degre -51HRC, 500 degre {{13 }}HRC,550 degre -38HRC,600 degre -33HRC,650 degre -29HRC.
Pwopriyete mekanik
Pwopriyete mekanik 60SI2MN Spring Steels yo dekri nan tablo ki anba la a.
| Fòs rupture | Kondisyon yo bay fòs | Elongasyon | Rediksyon nan zòn | Dite (woule cho) | Dite (desine frèt) |
| σb (MPa): Pi gran pase oswa egal a 1274(130) | σ0.2 (MPa): Pi gran pase oswa egal a 1176(120) | δ10 (pousan): Pi gran pase oswa egal a 5 | ψ (pousan): Pi gran pase oswa egal a 25 | Mwens pase oswa egal a 321HB; | |
Aplikasyon
60SI2MN asye, Mete aksan sou avantaj la se bon hardenability, yon lòt pèfòmans cho k ap travay, pwopriyete mekanik konplè,
Rezistans dekarburizasyon tou se bon gwo koup transvèsal nan divès sezon prentan enpòtan, tankou otomobil, lokomotiv, gwo sezon prentan plak, prentan, elatriye 60SI2MN Prentan prensipal yo itilize pou machin lou, traktè, chaj pwodiksyon endistriyèl, estrès ak dyamèt prentan an plak pi gwo. ak sezon prentan hélicoïdal