430 Nerjaveèi gen limite soudabilite epi li pa ta dwe itilize nan kondisyon an kòm soude pou estrikti dinamik oswa enpak chaje. Kòm yon materyèl feritik, 430 ka ka zo kase frajil nan tanperati ki anba zewo, epi yo pa ka itilize nan aplikasyon kriyojenik. Kòm asye a pa gen nikèl oswa molybdène, li pi bon mache pase nenpòt nan asye seri 300 la.
| Klas | C | Mn | Si | P | S | Kr | Mo | Ni | N | |
|---|---|---|---|---|---|---|---|---|---|---|
| 430 | min. max. | - 0.12 | - 1.00 | - 1.00 | - 0.040 | - 0.030 | 16.0 18.0 | - | - 0.75 | - |
| 430F | min. max. | - 0.12 | - 1.25 | - 1.00 | - 0.06 | 0.15- | 16.0 18.0 | - | - | - |
Soude
To perform any welding, stainless steel grade 430 has to be pre-heated at 150-200 degree (302-392 degree F). In case of embrittlement in the welded metal, the particular area can be post-weld annealed at 790-815 degree (1454-1499 degree F); however grain refinement will not happen.
Li rekòmande ke klas 430, 308L, 309 oswa 310 baton filler ta dwe itilize baze sou aplikasyon an.
Baj popilè: tiyo 430 Nerjaveèi asye, Lachin, Swèd, manifaktirè, faktori, achte, pri, lis pri, pou vann, nan stock, echantiyon gratis